E te masani ile nickel-chromium carbide?

(E masani ona taʻua o le NiCr-Cr₃C₂ composite powder) o se mea faʻapipiʻi maualuga faʻatinoga ua fuafuaina mo siosiomaga maualuga-vevela, pala, ma le ofuina. E aofia ai le nickel-chromium alloy (NiCr) fa'apipi'i vaega ma le chromium carbide (Cr₃C₂) vaega malo. O lona tuufaatasiga masani o le 75% Cr₃C₂ + 25% NiCr (lea o le NiCr o le 80% Ni ma le 20% Cr). O pa'u fa'apipi'i e ala i le suau'u okesene maualuga (HVOF) po'o le su'iina o le plasma e iai sona sao taua i le puipuia o vaega taua o fale gaosi oloa.

I. Meafaitino Tulaga ma Fauga

Fuafuaga tu'ufa'atasi o le Duplex:

Vaega Malosi Cr₃C₂: E iai se mea e liusuavai ai e oo atu i le 1810°C, e sili ona lelei le maa'a maualuga (microhardness 2200–2700 kg/mm²), ma le malosi e tetee atu i le oxidation (e na'o le 1100–1400°C e amata ai le oxidation taua). Vaega fa'apipi'i o le NiCr: E maua ai le malosi ma le fa'asao. O le 80% Ni-20% Cr alloy composition e fausia ai se ata oxide mafiafia i le vevela maualuga, faʻaleleia le pala ma le faʻamaʻiina.
Fua Pa'u: Fa'atupuina e ala i le fa'aputu'e ma fa'agasologa o le sintering, o le pa'u e masani lava ona iai le lapo'a o le 15-45 μm (mo le HVOF) po'o le -325 mesh (mo le su'iina o le plasma). Taofi ese mai le susu ma faʻagogo i le 120°C mo le itula e tasi aʻo leʻi faʻaaogaina.

II. Tulaga Autu o Galuega
1. Tulaga Maualuluga Maualalo
- Oxidation tetee e oʻo atu i le 900°C. A maeʻa ona faʻaalia i le 982 ° C mo le 5 itula, e faʻaalia ai naʻo sina lanu, ae o WC-Co alloys poʻo uʻamea uʻamea e aʻafia ai le faʻamaʻiina o le faʻamaʻi.
- Fa'amauina maualuga le ma'a'a i le maualuga o le vevela e talafeagai ai mo masini fa'amama e pei o kesi kesi ma fa'avela.

2. Lelei Fa'aleaga Tetee
- I totonu o siosiomaga sulfuric acid dilute, o lona tetee corrosion e 30 taimi nai lo 1Cr18Ni9Ti stainless steel; i siosiomaga ausa, o lona tetee corrosion e 50 taimi nai lo Co-WC alloys.
- Tete'e i le alkaline solution corrosion, talafeagai mo le gaosiga o pepa ma mea tau vaila'au.

3. La'ei maualuga ma Tete'e o le tafia
- A mae'a ona fa'asusu i luga o puipui fa'apau fau paoa, e fa'aitiitia le la'ei fa'aletausaga mai le 1.5-2.0 mm i le 0.03 mm, fa'ateleina le ola tautua i luga atu o le 7 tausaga.
- E sili atu le tete'e atu i le tafia e ala i le tafe mai o le oneone, e talafeagai mo lau o le turbine ma vaega o pamu o le gataifale.

4. Fa'ata'ita'iina Fa'atinoga o Feese'esea'iga (Vaega Fa'a'u'u Tagata Lava)
- O le fa'aopoopoina o le Ni-coated MoS₂ (8-24%) e fa'atupuina ai le fa'apalapala o le tagata lava ia, fa'aitiitia ai le fa'a'ese'esega mai le 0.72 i le 0.45 ma fa'aitiitia ai le pa'u o le mamafa i le 36%.

III. Talosaga Alamanuia
1. Malosiaga ma Meafaigaluega Malosiaga
Puipuiga "Four-Tube": O paipa vai-puipui, superheaters, ma isi, e puipuia mai le tafia o le pefu koale, faʻateleina lo latou ola tautua i le 7 taimi, faʻaitiitia le paʻu.
Gas Turbines ma Hydropower: Faʻapipiʻi faʻamaʻi-cavitation i luga o faʻamaufaʻailoga mata ma taʻiala taʻiala, faʻafefe i le 800°C maualuga-vevela kasa.

2. Petrochemicals ma Masini Mamafa

Meafaigaluega vili: Kola vili ma laina pamu palapala e tetee atu i le tafia o le palapala ma le pala ole acid vaivai.

Valves ma Compressors: Fa'amau fa'amau ma fa'avili fa'amau e fa'amalosia e sui ai mea taugata maualuga.

3. Masini Fa'apepa ma Ie

Fa'amamago Laua'i Lau'ele'ele: Ma'a'a e o'o i le HRC 35-46, fa'aitiitia ai le ofuina o le siki ma fa'alautele le taamilosaga mai le ono masina i le 3-4 tausaga.

Gondola Rollers: Tete'e alava fe'ese'esea'i ma fa'alautele suiga suiga.

4. Aerospace ma Mea Maualuga Maualuga

Fa'ailoga Fa'ailoga Inisinia: Fa'amau fa'amau fa'amau fa'apipi'i e fa'aalia ai le malosi fa'amau o le 43-47.6 MPa ma mea e fa'aulu ai le tagata lava ia.

Pins Mea e Fa'atula'i Tu'ueleele: Tetee atu i le fa'afuifu ma fa'ateteina a'afiaga maualuga.

IV. Manatu Autu i le Fa'agasologa o le Sausau
1. Pa'u Feso'ota'i
- Mo le HVOF, -325 mesh pa'u lelei (tele matolu 15-45 μm) e sili; mo le fufuluina o le plasma, -150/300 mesh e filifili.
- E mana'omia e le pa'u o le Hygroscopic le fa'avevela ile 120°C mo le itula e tasi e puipuia ai le posity ile ufiufi.

2. Parameter Optimization
HVOF faagasologa: Saosaoa afi 1500–2000 m/s, vevela 2800–3100°C, taofiofia le Cr₃C₂ pala (fua o le decomposition - Fa'ailoga masani: Oxygen pressure 0.9 MPa, propane pressure 0.4 MPa, fa'afefe mamao 180–380 mm.

3. Fa'ameamea Mu'ai Togafitiga
- Sandblast i le vasega Sa3, ma le talatala o le 50-80 μm. E tatau ona fa'amae'a le su'iina i totonu o le 3-4 itula talu ona fa'amama oneone.

V. Fa'atonuga ma Fa'asologa
Fa'apipi'i Fa'alu'u a le tagata lava ia: O le fa'aopoopoina o lubricant mautu e pei ole Ni-coated MoS₂/BaF₂ e fa'aitiitia ai le fa'atatau o fete'ena'iga (fa'ata'ita'iga, i fa'amaufa'ailoga aerospace).
Nano-faʻaleleia: Faʻafeiloaʻi le B₄C poʻo le nano-Cr₃C₂ (0.8-2 μm) faʻaleleia le mamafa o le ufiufi ma le faigata.
Fa'ata'ita'iga Atamai: Mata'ituina taimi tonu o le vevela o le mumu ma le saosaoa o mea'ai e fa'aitiitia ai le porosity fa'apipi'i (taulia:

Aotelega
O lapisi nickel-chromium carbide, e ala i la latou mamanu faʻatasi o se "Cr₃C₂ vaega faigata + vaega faʻapipiʻi NiCr," o se fofo lelei mo le faʻatalanoaina o le faʻatolu ona toilalo o le maualuga o le vevela, pala, ma le ofuina. O lo latou faʻaaogaina faʻamaonia i le malosi, vaalele, ma alamanuia mamafa ua faʻamaonia ai lo latou aoga puipuia umi. O le atina'e i le lumana'i o le a taula'i atu i mea tu'ufa'atasiga tele ma fa'agaioiga sa'o e fa'aauau ai le fa'ato'ilaloina o fa'alavelave i le puipuiga i lalo o tulaga ogaoga o galuega.